| Coating-refining flux |
- Melt refining from non-metallic inclusions
- Cover protection of the melt against oxidation
- Minimizing the loss of aluminum with dross
- Provides the formation of dry, well-removable dross
|
| Coating-refining flux with modifying effect |
- Modification of eutectic silicon
- Melt refining from non-metallic inclusions
- Provides the formation of a protective coating layer on the surface of the melt
- Provides the formation of dry, well-removable dross
- Minimizing the loss of aluminum with dross
|
| Special coating-refining flux for the removal of magnesium and alkaline earth metals from aluminum alloys |
- Removal of magnesium and other alkaline earth metals from aluminum alloys
- Recommended to use in complex with Special degassing tablet for the removal of magnesium and alkaline earth metals (Specification BY 14744129.004-98)
|
| Coating-refining cleansing flux for the removal of crusts |
- Removal of outgrowths and crusts of dross from the walls of furnaces, ladles and other equipment
- Minimizing the loss of aluminum with dross.
|
| Coating-refining flux for the treatment of hypereutectic silumins |
- Cover protection of the melt surface from the oxidation of an alloy with a silicon content of more than 12%
- Minimizing the loss of aluminum with dross
|
| Coating-refining self-melting flux |
- Special flux for high-level melt refining
- Formation of a cover-protective liquid layer on the melt surface
- Minimizing the loss of aluminum with dross
- Recommended for metallurgical re-melting of dross
|
| Universal flux for deformable alloys |
- Creation of a protective coating layer on the melt surface
- Obstruction of the dissolution of gases H2, O2 in liquid deformable alloys
- Cleaning of melts from non-metallic inclusions and micro impurities
- Reducing the overgrowing of the furnace lining
|
| Flux preparation PF-1 |
- Creation of a protective coating layer on the melt surface
- Adsorption of gases and non-metallic inclusions during the refining-degassing treatment
- Reduction of the overgrown walls of the furnace lining
- Applies on aluminum-based alloys, including deformable alloys
|
| Flux complex composition |
- Degassing and refining of the melt from non-metallic inclusions
- The formation of dry, well-removed dross
- Reduction of overgrown furnace lining
- Creation of a covering protective layer on the melt surface
- Recommended for metallurgical remelting of scrap aluminum-based alloys
|
| Flux complex composition with modifying effect |
- Modification of the eutectic (Al+Si)
- Refining of pre-eutectic and eutectic silumin from non-metallic inclusions and gases
- Grinding alloy structure
- Formation of dry, well-removable dross
- Creation of a covering protective layer on the melt surface
- Can be used in liquid (molten) state
- Long preservation time of modifying effect (up to 2 hour)
|
| Flux complex composition for rotary furnaces with horizontal axis |
- Intended for metallurgical re-melting of fine-dispersed aluminum-containing materials (chips, scrap, dross), in rotary furnaces using gaseous or liquid fuel
- Provides maximum metallurgical output of aluminum
|
| Flux complex composition for rotary furnaces with inclined axis |
- Intended for metallurgical re-melting of fine-dispersed aluminum-containing materials (chips, scrap, dross), in rotary furnaces using gaseous or liquid fuel
- Provides maximum metallurgical output of aluminum
|
| Flux complex degassing composition |
- Deep volume degassing of the melt
- Melt refining from non-metallic inclusions
- Increase of metal density in castings
- Minimizing the loss of aluminum with dross
|
| Refining-modifying preparation for treatment of non-ferrous alloys PRM-1 |
- Melt refining from non-metallic inclusions
- Removal of outgrowths and crusts from the walls of furnaces, ladles and other equipment
- Minimizing the loss of aluminum with dross
- Highly effective in alloy treatment in induction furnaces
|
| Refining-modifying preparation for treatment of non-ferrous alloys PRM-2 |
- Melt refining from non-metallic inclusions
- Used by blowing under the surface of the melt in the gas carrier stream (N, Ar), as well as in the ladle when overflowing from the furnace
|
| Refining-modifying preparation for treatment of non-ferrous alloys PRM-3 |
- Effective refining treatment of aluminum alloys in furnaces of various designs, in ladles
- Minimization of losses of aluminum with dross
- Wide application temperature range (645ºС…800ºС)
|
| Refining-modifying preparation for treatment of non-ferrous alloys PRM-4 |
- Modification of the eutectic (Al-Si)
- Increase of physical and mechanical properties (ultimate tensile strength, yield strength, elongation)
- Improvement of technological properties of aluminum piston alloy
- Wide application temperature range (645ºС…800ºС)
|
| Flux preparation PF-6 |
- Effective refining of Al-Mg, Al-Si-Mg
- Formation of dry, well-removable dross
- Minimization of losses of aluminum with dross
|
| Flux preparation PF-8 |
- Removal of outgrowths and crusts of dross from the walls of furnaces, ladles and other equipment
- Provides extended furnace lining life
- Melt refining from non-metallic inclusions
- Minimization of losses of aluminum with dross
|